Luvocom 3F PEEK CF 9676 is a 3D printing filament made from carbon-fibre reinforced PEEK (Polyether Ether Ketone). The carbon fibres in Luvocom 3F PEEK CF 9676 filament significantly improve the stiffness and compressive strength of 3D printed parts.
This material enables industrial 3D printing applications in numerous sectors, including aerospace, medical, oil & gas, energy, marine and automotive. In these areas, it can be used to produce components that can replace traditional metal or composite parts.
Parts printed with Luvocom 3F PEEK CF 9676 are suitable for applications exposed to operating temperatures of up to 280°C for short periods and continuous temperatures of up to 250°C.
This filament is suitable for 3D printing of dynamically stressed parts, chemical and hydrolysis resistant parts, non-flammable components and applications requiring intrinsic flame resistance with low smoke and toxic gas emissions.
Key features
- Contains Lehvoss Luvocom 3F PEEK CF 9676 BK
- Suitable for applications with continuous operating temperature up to 250°C
- Short-term operating temperature up to 280°C (max. 200 hours during life cycle)
- Thermal deflection temperature: 280°C
- Very high rigidity and strength (also in Z-direction)
- Excellent mechanical properties
- Non-flammable
- Outstanding chemical resistance
Applications
- Components subjected to dynamic stress
- Highly chemically resistant parts
- Hydrolysis-resistant components
- Aerospace applications
- Automotive
The PAEK family
PolyArylEtherKetone (PAEK) is a family of high-performance semi-crystalline thermoplastics characterised by high mechanical strength and excellent resistance to temperature, chemicals and wear.
The most popular members of the PAEK thermoplastics family are:
- PolyEtherEtherKetone (PEEK)
- PolyEtherKetoneKetone (PEKK)
- PolyEtherKetone (PEK)
- PolyEtherEtherKetoneKetone (PEKEKK)
- PolyEtherEtherKetoneKetone (PEEKK)
General printing guidelines *
| Nozzle size: ≥ 0,4 mm |
Height layer: ≥ 0.10 mm |
Experience level: Expert |
| Print temperature: ± 400 - 450°C |
Fan speed: 0 - 25%. |
Drying: +4 hours at max. 110°C |
| Heated plate: ≥ 120°C |
Closed chamber: heated chamber at 90°C |
Adhesion to substrate: EasyFix No. VII |
* The above settings are guidelines for finding optimal print settings. These ranges should work with most printers, but you can experiment outside these values if you feel it is suitable for your printer. There are many different types of printers, hot-end and offset, so it is difficult to provide universal settings that apply to all.
Abrasivity
The filament LUVOCOM 3F PEEK CF 9676 BK contains a high concentration of extremely hard carbon fibres, which have an abrasive nature.
In general, these fibres accelerate the wear of brass nozzles much faster than unreinforced filaments.
It is therefore recommended to use nozzles made of stainless steel or hardened alloys.
Filament length
| ρ: 1.36 g/cc |
Spool 0.2 kg |
Spool 0.5 kg |
| Ø 1.75 mm |
± 61 m |
± 153 m |
| Ø 2.85 mm |
± 23 m |
± 58 m |
Package contains: 1 x LUVOCOM 3F PEEK CF 9676 - Formfutura